Přednášející: Sergey Varlamov (University of New South Wales, Sydney, Australia)
Místo: Cukrovarnická 10, budova A, knihovna, 1. patro
Jazyk: anglicky
Pořadatelé:
Oddělení tenkých vrstev a nanostruktur
Liquid-phase crystallisation of a few micron thick Si films on glass (LPCSG) allows obtaining a high crystal and electronic quality material which is a promising alternative to c-Si wafers for photovoltaics. Potentially capable of matching c-Si wafer cell performance, LPCSG needs no wafering process and can also benefit from monolithic cell-module integration typical for thin-film technologies. Crystallisation can be conducted either by line shaped e-beam source (in vacuum) or by line-focused diode laser (in air). The resulting material consists of tens of millimetres long and up to a millimetre wide linear grains roughly aligned in a scan direction. Intragrain defect density is less than 1E7 cm-3 and the carrier mobility is as high as 410 cm2/Vs, both comparable to respective values in mc-Si wafers. Solar cells made of LPCSG films have achieved open circuit voltages up to 630 mV and efficiencies of 11.7%, and improvement in the cell performance continues at a fast rate since the material introduction in 2011. Quite surprisingly, the most of the performance improvement is achieved due to development of an intermediate layer between glass and Si. Regarding the Si film material itself, as long as crystallisation in conducted in a laser parameter range between full melting and dewetting, no significant effects of various process parameters on the material quality and cell performance are observed. The intermediate layer is thus most critical to cell fabrication and it has to satisfy a few very important requirements: very high temperature stability; wetting and adhesion; transmission and antireflection; impurity diffusion barrier; dopant source; interface passivation. High melting point transparent dielectrics, such as SiCx, SiNx and SiOx have been studied as intermediate layers. It is found than no single layer can perform all functions. SiCx is the best adhesion layer but it has high absorption, poor barrier and interface passivation properties; SiNx is good for transmission and antireflection but the worst for adhesion and impurities; SiOx is the best for transmission, passivation, as an impurity barrier and provides reasonably good adhesion but it has no antireflection effect. Only a carefully designed combination of dielectric layers can deliver both the robust fabrication process and well-performing cells. Triple-layer stacks of SiOx/SiCx/SiOx and SiOx/SiNx/SiOx are developed where the middle layer is for antireflection while the outer layers are for adhesion, impurity blocking and interface passivation. The presentation gives more details on laser-crystallised Si film and solar cell fabrication and associated effects of the intermediate layer. ---------------------------------------------------------------------------------------------------------------------------------- Dr Sergey Varlamov is a Senior Research Fellow and Si thin-film solar cell group leader at University of New South Wales in Sydney. He received a PhD award in chemistry at Moscow State University in 1987, worked as a researcher for Russian Academy of Sciences in the area of biologically active compounds and then in Japan where he changed his career to thin-film technologies. He moved to Australia in 1995 to join UNSW to work on crystalline Si-on-glass solar cells and a few years later became a group leader. The group’s focus is on Si deposition processes, film crystallisation, thin-film solar cell design, metallisation and light-trapping. Currently Dr Varlamov research priority is diode laser crystallised Si thin-film solar cells. His group has made a major contribution to the Si-on-glass technology resulting in solar cells with the world best efficiencies.
Copyright © 2008-2010, Fyzikální ústav AV ČR, v. v. i.